Fireproof Fiberglass Fabric High Silica Fabric Glass Fiber Cloth
1. Description:
High Silica Fabric is made of silica fiberglass. It is an inorganic fiber, that contains more than 96% SiO2. It's resistant to high temperatures (melting point) 1700℃, and longtime service temperatures 900℃. It can work for 10 minutes at 1450℃ and keeps a good state at 1600℃ for 15 seconds, for its properties of chemical stability, high-temperature resistance, and ablation resistance. It is widely used in aviation, aerospace, metallurgy, chemical, building material, and fire-fighting industries.
2. Technique Data Sheets for High Silica Cloth
| 1 | WEAVE | SATIN 8HS | Testing Method |
| 2 | Width | 92cm | 36.2inch | DIN EN 1773 |
| 100cm | 39.4inch |
| 86cm | 33.1inch |
| 3 | SiO2 Content | ≥96% | - |
| 4 | Linear shrinkage ( 1000C 30min) | <7.10% | - |
| 5 | Area Shrinkage( 1000C 30min) | <13.0% | - |
| 6 | Color | White / Golden | - |
| 7 | Thickness | 1.3±0.1mm | 0.051inch | DIN EN ISO 5084 |
| 8 | Treatment | Hydrochloric acid treatment | - |
| 9 | Weight | 1100g/m2 | 32.4OZ/YD2 | DIN EN 12127 |
| 10 | Thread count | WARP | 20 per cm | 51 per inch | DIN EN 1049-2 |
| WEFT | 15 per cm | 38 per inch | DIN EN1049-2 |
| 11 | Tensile strength | WARP | ≥1100 | EN ISO 13934-1 |
| N/Inch | WEFT | ≥900 | EN ISO 13934-1 |
| 12 | Service temperature | Up to 1100ºC | - |
3. Features:
1. SiO2 Content ≥ 96%
2. Soft point nearly 1700oC, long-period service at 1000oC
3. Low thermal conductivity
4. Low thermal shrinkage
5. Good Chemical Stability
6. Good Electrical Insulation
7. Good Process Performance
8. Non-asbestos, zone-pollution
4. Application:
High temperature resistant, insulation and sealing material
High-temperature ablation resistant material
Fireproof material for fireproof protective cloth, fireproof curtain
Dust collection in media of high-temperature gas
Filter for molten metal
Extinguisher insulation material
Protective material for welding
electricity insulation material
5. Product Detail Images
6. More Silica Cloth Specification
| Product Name | Model | Width mm | Working Temperature℃ | Weight g/㎡ | SiO2 Content |
| High Silica | JNHS-300-92 | 92 | 1000 | 300 | ＞96% |
| High Silica | JNHS-450-92 | 92 | 1000 | 450 | ＞96% |
| High Silica | JNHS-600-92 | 92 | 1000 | 612 | ＞96% |
| High Silica | JNHS-600-100 | 100 | 1000 | 612 | ＞96% |
| High Silica | JNHS-600-130 | 130 | 1000 | 612 | ＞96% |
| High Silica | JNHS-880-92 | 92 | 1000 | 880 | ＞96% |
| High Silica | JNHS-880-100 | 100 | 1000 | 880 | ＞96% |
| High Silica | JNHS-1100-92 | 92 | 1000 | 1100 | ＞96% |
| High Silica | JNHS-1100-100 | 100 | 1000 | 1100 | ＞96% |
| Silica Cloth | JNSC-450-100 | 100 | 800 | 600 | 70%±5% |
| Silica Cloth | JNSC-600-92 | 92 | 800 | 600 | 70%±5% |
| Silica Cloth | JNSC-600-100 | 100 | 800 | 700 | 70%±5% |
| Silica Cloth | JNSC-600-152 | 152 | 800 | 700 | 70%±5% |
| Silica Cloth | JNSC-1100-92 | 92 | 800 | 1100 | 70%±5% |
| Silica Cloth | JNSC-1200-100 | 100 | 800 | 1200 | 70%±5% |
| Silica Cloth | JNSC-1200-152 | 152 | 800 | 1200 | 70%±5% |
| High Silica Texturized Cloth | JNSCT-42-92 | 92 | 1000 | 1450 | ＞96% |
| High Silica Texturized Cloth | JNSCT-42-100 | 100 | 1000 | 1450 | ＞96% |